ABSTRACT Brazilian flora has more than 12 thousand tropical wood species, which can be the raw material for the construction industry. Chromated copper borate (CCB) and chromated copper arsenate (CCA) are wood preservative chemicals, which can generate toxic waste. Particleboards are usually produced from Pinus sp. and Eucalyptus sp. wood particles and a polymeric matrix (often formaldehyde-based), and they are used as raw material mainly for the furniture industry. This study aimed to investigate the technical feasibility of particleboard production using caixeta wood (Simarouba amara Aubl.) particles and bicomponent castor oil-based polyurethane resin for tropical wood waste management, as well as study the impact of CCA/CCB treatments on the performance of these panels according to NBR 14810 standards. Analysis of variance (ANOVA) tests was performed to compare ten physical and mechanical properties of the panels produced with CCA, CCB, and non-treated caixeta wood particles. The performance of caixeta wood panels was similar to the usually produced boards (using Pinus sp. and Eucalyptus sp. wood). Furthermore, preservative treatments did not change significantly the mechanical performance of panels. However, water absorption increased and thickness swelling decreased in CCA/CCB treated samples.

ABSTRACT Wood is one of the main materials used in the constructing of covering structures (roofs) because of its versatility. Under this situation, due to solar radiation incidence, the temperature can exceed 60 °C and, such as other environmental conditions, influence the mechanical properties of the wood in use. The aim of this research was to study the influence of exposure time of the wood of four different hardwood species at a temperature of 60 °C on the shear strength parallel to fibers. The wood of the following species was used: Cupiúba (Goupia glabra), Eucalyptus (Eucalyptus saligna), Garapeira (Apuleia leiocarpa), and Jatobá Tamarindo (Hymenaea sp.). In order to investigate the effect of exposure time (0, 168, 456, 720, and 2160 hours) of the wood species in an oven (60 °C) on the values of shear strength in the direction parallel to fibers, an analysis of variance (ANOVA) was carried out at 5% significance level. According to the results, the time the wood was exposed to the operating temperature significantly influenced the shear strength in the direction parallel to fibers. In addition, all species showed a decrease in shear strength after 456 hours of exposure at a constant temperature of 60 °C.

ABSTRACT The aim of this research was to analysis the feasibility of production of wood particleboard with two alternative adhesives: epoxy ink waste and polyhydroxybutyrate polymer (BTH). Particleboard were produced with Pinus sp. wood specie wastes from sawmill process. For each alternative adhesive was proposed different combinations of parameters: time and temperature of press, pressure; alternative adhesive content and mass of wood particles. Two alternative adhesive contents were adopted, 10% and 20% replacing ureaformaldehyde adhesive. Mechanical properties (perpendicular tensile strength, pullout strengths of screw on face and top; modulus of elasticity and rupture) were determined according to ABNT NBR 14810:3 Brazilian Standard Code. The obtained results were compared to ABNT NBR 14810:3 and ANSI A.2018:1 Standard Codes requirements values. Particleboards produced with epoxy ink waste showed perpendicular tensile strength according to the minimum Standards requirements values. All proposed combinations to manufacture BTH polymer particleboards didn't show satisfactory mechanical properties in comparison to the Standard Codes values. Other combinations of wood species, time, pressure and temperature, epoxy ink waste and BTH polymer contents should be studied so that the requirements can be met.